1 BF damage, the causes for lining and cooling line damage and the effect of titanium slag protection were analyzed.
本文总结了包钢 1# 高炉 2 0 0 1年大修停炉后炉体破损情况 ,分析了砖衬和冷却壁的破损原因和钛渣护炉效果 ,并就延长高炉寿命提出了几点建议。
This paper shows the actual results of increasing lining life has been achieved by using technology widely to build the singlecourse-brick lining of the converter in the world, in order to save the problems of converter's inner shape and its lining material in PISC.
针对攀钢转炉炉型、炉衬材质存在的问题，采用当今世界上普遍采用的单层砖衬砌筑工艺，取得了转炉炉龄提高的明显实效。