Effect of roasting process on the shrinkage rate and compressive strength of silica sol ceramic mold was investigated.
采用胶态成型技术和优化的真空干燥工艺制备硅溶胶陶瓷型干坯料,并探讨焙烧工艺对其收缩(率)和抗压强度的影响。
The shrinkage mechanisms and shrinkage process of the injection plastic products are analyzed, with the effects of process conditions on the shrinkage rate, such as average mold cavity pressure of the PA injection molding, molten mass temperature, mold temperature, mold filling up speed rate etc.
分析了注塑制品的收缩机理及收缩过程,并讨论了聚酰胺(PA)注射成型过程中模腔平均压力、熔体温度、模温、充模速率、成型时间等工艺条件对其收缩(率)的影响及制品后收缩(率)的因素,给出了减小制品收缩(率),提高制品尺寸稳定性的方法。
The experiment shows that the shrinkage rate of wool fabric is mainly influenced by drying transfer speed, enviroment temperature and humidity.
通过对毛料织物进行干燥实验,对毛料收缩(率)的影响因素进行了探讨,实验结果表明:毛料收缩(率)主要受干燥时传输速度、环境温度、环境湿度的影响。
Effect of dry acrylic tow processing on bulky top shrinkage;
影响干法腈纶毛条收缩(率)的因素探讨
Study on Shrinkage of BIG CPUE Product;
大型浇注型聚氨酯弹性体制品收缩(率)的研究
Analysis of Affecting Factors of Shrinkage of Injection Molding;
注塑成型收缩(率)影响因素的分析
Select shrinkage ratio according to style of plastic parts;
塑件类型与收缩(率)的选用
The expectancy of shrinkage ratio(drying shrinkage ratio and total shrin.
重复试验得到硅溶胶陶瓷型收缩(率)(干燥收缩(率)和总收缩(率))和抗压强度的期望为0。
DMAc was selected as solvent and Polyvinylpyrrolidone (PVP K90) was selected as pore forming additive, the influence of Polyvinylpyrrolidone concentration on the shrinkage ratio, the pure water flux, the retention to BSA and the membrane structure of Poly(vinylidene fluoride)/polyethersulfone Blend Membranes were investigated.
采用二甲基乙酰胺为溶剂,聚乙烯吡咯烷酮(PVPK90)为致孔性添加剂,研究了PVP的浓度对聚偏氟乙烯/聚醚砜(PVDF/PES)共混膜的收缩(率)、纯水通量、牛血清蛋白(BSA)截留率和膜结构的影响。
The effects of pyrolysis temperature and soaking time on ceramic yield,linear shrinkage,mechanical properties and microstucture were investigated.
研究了热懈温度和保温时间对陶瓷产率、线收缩(率)、力学性能以及微观结构的影响。
The effects are investigated of nano-Al_2O_3powder additive on sintering behaviors of alumina ceramics,such as volume density,water-absorbing rate,porosity,linear shrinkage.
研究了纳米A l2O3粉添加对粗晶氧化铝陶瓷烧结行为,如体积密度、吸水率、气孔率、线收缩(率)的影响。
The microstructures and properties such as linear shrinkage, ceramic yield and flexural strength of active filler Al_containing polycarbosilane(PCS)_derived ceramics pyrolyzed at different temperatures were investigated.
研究了裂解温度对活性填料Al-聚碳硅烷裂解陶瓷的线收缩(率)、陶瓷产率、力学性能等的影响 。
The effects of solidified agent, nanometer silicon dioxide powder and calcium carbonate powder on line contraction percentage of silicon rubber mould were discussed in this paper.
本文主要研究了固化剂、纳米二氧化硅粉和碳酸钙粉等外加剂对硅橡胶模具线收缩(率)的影响。
The line contraction percentage of the sintered samples were investigated.
通过在原料中添加磷酸盐玻璃粘接剂改善HA生物陶瓷的烧结性能,测定试样的线收缩(率),研究了粘接荆对HA植入体烧结的影响。
Effect of PET film heat shrinkage rate on loss angle tangent value of capacitor charge-discharge process;
聚酯薄膜热收缩(率)对电容器充放电后损耗角正切值的影响
The discussion also covered the influence of mold design and product structure on the shrinkage ratio and the factor of after shrinkage ratio.
分析了注射制品的收缩机理及收缩过程,并讨论了结晶型塑料注射成型过程中模腔平均压力、熔体温度、模温、充模速率、成型时间等工艺条件和模具设计、制品结构对其收缩(率)的影响及制品后收缩(率)的因素,给出了减小制品收缩(率),提高制品尺寸稳定性的方法。