In order to improve detection precision, the method of detecting T-type fillet weld lack of penetration height was discussed using ramp probe in the wing.
为提高检测精度,探讨了用斜探头在翼板上检测T型角焊缝未焊透高度的方法。
The tensile experimental results of four group L 3R welding test specimen included defect free and with above plate part,defect free and no above plate part,with lack of penetration and above plate part,with lack of penetration and no above plate part were presented in this work.
报道了L3 R焊接试板在无缺陷有焊缝余高、无缺陷无焊缝余高、有未焊透有焊缝余高、有未焊透无焊缝余高四组试样的拉伸试验结果和L3 R热轧板和焊接板的裂纹张开位移试验结果。
The lack of penetration (LOP) is a very common type of discontinuities in welds,so that how to simplify it more scientifically and reasonable and therefore to conduct its fracture analysis are a problem continuously interested to engineering and academic circles.
未焊透是工程实际焊接结构中最为常见的一种焊接不连续 ,如何更科学合理地简化未焊透工程 ,以便于对其进行的断裂分析是工程界和学术界所一直关心的问题。
Ultrasonic detecting method of incomplete penetration depth of T-joint weld;
T型接头组合焊缝未焊透深度的超声检测方法
Effects of incomplete penetration on the stress concentration of lattice frame empty spheric joint;
未焊透对网架空心球节点应力集中的影响
However, the researches into the pipe tees with incomplete penetration defects are inadequate.
三通是压力管道系统中不可缺少的管道元件,但国内对存在未焊透缺陷的三通研究很少。
?The structure of the ellipse tube with incomplete penetration defects is investigated.
应用有限元法对未焊透的椭圆接管结构进行了应力数值分析,并应用压力容器分析设计法,对该结构进行了疲劳分析,得出结构因未焊透缺陷导致疲劳破坏。
Incomplete penetration defect is one of common defects in industrial pressure piping system, few researches was reported at home and abroad.
未焊透缺陷是工业压力管道系统中广泛存在的一种焊接缺陷,国内外对此类压力管道缺陷的研究较少。