However,laboratory tests and field experience indicates the 13 Cr steel undergoes inter-granular stress corrosion cracking(IGSCC) in the heat affected zone of the welds.
但是实验室试验和现场经历表明,13Cr马氏体不锈钢焊接接头热影响区发生了沿晶应力腐蚀开裂(IGSCC)。
On behavior of sulfide-stress corrosion cracking (SSCC) of X80 pipeline in H_2S environment;
X80焊管H_2S环境应力腐蚀开裂行为研究
The stress corrosion crack causes of high sulfur pipes serviced hydrodesulfurization system of a refinery were analyzed.
表明管道的开裂是由富含H_2S环境介质再加上焊缝附近较高的焊接残余应力引起的应力腐蚀开裂。
The susceptibility to stress corrosion cracking (SCC) of the welded joint of X80 pipeline steel in solution of 0.
5mol/LNa2CO3+1mol/LNaHCO3溶液中的应力腐蚀开裂(SCC)敏感性。
nitrate cracking
热硝酸盐应力腐蚀开裂
sulfide-stress cracking
硫化物应力腐蚀开裂
Study on SCC of the 2A12 Hard Aluminum Alloy Used in Aircraft;
飞机用硬铝2A12应力腐蚀开裂研究
Inhibitive Action of Benzotriazole for SCC of 18-8 Stainless Steel
苯并三氮唑对18-8钢应力腐蚀开裂的缓蚀作用
High environment humidity increases the susceptibility to hy-drogen induced cracking and stress corrosion cracking.
高湿度能增大氢致裂纹和应力腐蚀开裂倾向。
Study on Stress Corrosion Cracking of 304L Stainless Steel in Caustic Solution at High Temperature;
304L在高温碱性溶液中应力腐蚀开裂的研究
Study on Electrochemical Noise for Stress Corrosion Cracking of C Ring Specimen;
C型环试样应力腐蚀开裂的电化学噪声研究
Resistance to H_2S Stress Cracking of NK-HITEN610U2 Steel Plate and Its Welded Joint
NK-HITEN610U2钢板及其焊接头抗H_2S应力腐蚀开裂性能
Experimental Study on Stress Corrosion Cracking of 2.25Cr1Mo Steel in H2S Solution
2.25Cr1Mo钢在硫化氢溶液中的应力腐蚀开裂研究
Stress corrosion cracking behaviour of two stainless steels in hydrogen sulfide environment
硫化氢环境下两种不锈钢的应力腐蚀开裂行为
STRESS CORROSION CRACKING OF X56 GRADE PIPELINE STEEL IN ATMOSPHERIC ENVIRONMENT CONTAINING H_2S
API X56钢在含H_2S的海洋大气中的应力腐蚀开裂
SCC of Oil and Gas Pipeline in High-pH Environment
油气管道在高pH值环境下的应力腐蚀开裂
Investigation of Restriction on Hydrogen Induced Cracking and Stress Corrosion Cracking of X80 Pipeline Steel
X80级管线钢抗氢致开裂和应力腐蚀开裂性能研究
Studying pipeline corrosion and stress corrosion cracking mechanisms, and developing models and techniques for predicting, inspecting, and preventing pipeline failure.
研究管道腐蚀和应力腐蚀开裂机制，开展管道失效的预测模型和检测模型技术研究。
Research on Stress Corrosion Cracking of Typical Pressure Vessel Steels in Wet Hydrogen Sulfide Service;
典型压力容器用钢在湿硫化氢环境中的应力腐蚀开裂研究
Factors of Mechanics Influencing Stress Corrosion Cracking of Pipeline Steels in Near-neutral pH Environment
影响管线钢在近中性pH值环境中应力腐蚀开裂的力学因素
Effect of tempering temperature on stress-corrosion cracking and mechanical hysteresis of 2Cr13 stainless steel
回火温度对2Cr13不锈钢应力腐蚀开裂和力学滞后的影响
Influences of Concentration,Temperature and Strain Rate on Stress Corrosion Cracking of 316L Stainless Steel in Alkali Solution at High Temperature
高温碱液浓度与温度及应变速率对316L不锈钢应力腐蚀开裂的影响